Produse pentru component 2 epoxid (9)

Transparent epoxy coating of two components with high chemical and mechanical resistance for the protection and decoration of floors. Does not contain solvents (100% solids). Features High transparency. Excellent resistance to yellowing and water staining. Very good resistance to solvents, detergents, acids and diluted bases, gasoline, diesel, brake fluid and lubricating oils. High mechanical resistance. Antidust effect.

Syntech Poliurea Primer – Epoxy Metal Syntech Poliurea Primer – Epoxy Metal is a two-component primer based on epoxy resins free from solvents, used to promote adhesion, as a surface sealant for concrete, applied as a substrate for works with polyureas on metal surfaces and epoxy and polyurethane coatings. Adhesion promoter, surface sealant for concrete, to be applied as a substrate for works with polyureas on metal surfaces and epoxy and polyurethane coatings. The application must take place on a dry and degreased surface; the substrate must not have crumbly or detached parts and with a degree of humidity that must not exceed 5%. Preparation of the substrate may require some types of mechanical action: Smoothing, bush-hammering, shot peening, hydro-washing. Other mechanical actions that can make the support suitable. The individual components must be mixed carefully until a homogeneous mass is obtained. The material can be applied by roller, brush or spray by means of special airless machines, even in two coats. The temperature of the support must always be at least 3°C higher than the dew point temperature. Minimum application temperature +5°C, maximum temperature +35°C. Approximately 0,20 kg of Syntech Poliurea Primer – Epoxy Metal for every square metre of surface to be treated. Can 10 kg [A] - Can 5 kg [B] - Kit: 1 Can 10 kg [A] + 1 Can 5 kg [B]

Colles polymérisant à température normale ou par chauffage Température normal 50°C

Thermische Spritzverfahren Lichtbogenspritzen Atmosphärisches Plasmaspritzen Pulverflammspritzen Drahtflammspritzen Hochgeschwindigkeits-Flammspritzen (HVOF) Nachbehandlung von Spritzschichten Versiegeln Ofensintern Drehen/Schleifen/Läppen/Honen Qualitätssicherung von Spritzschichten Prüfen und Messen der Bauteile Prüfen auf Rissfreiheit Messen der Oberflächenhärte Messen der Oberflächenrauheit Erstellen eines metallographischen Schliffes

Durch unsere langjährige Erfahrung im Formenbau sind wir ein kompetenter Partner für die Konstruktion und Entwicklung von Formen, Vorrichtungen und Teilen aus Holz, und/oder Kunststoff und Beton Wir verfügen über alle Möglichkeiten zur Bearbeitung von Holz oder holzähnlichen Werkstoffen. Somit richten wir uns auch an verschiedenste Branchen der Industrie, das Handwerk sowie Planer. Ob bei der Entwicklung von Prototypen der Losgröße 1, Einzelstücken, Komplettfertigungen, Kleinserien oder Serienbauteilen. Wir begleiten Sie von den ersten Planungsprozessen bis zum Projektabschluss.

Epoxy waterborne paint bicomponent cured with polyamide, for protection of floors of concrete, metal structures, etc.

EG 91 Epoxy-polyurethane two-component elastoplastic and thixotropic sealant, for joints subject to traffic, where Shore A Hardness Scale = 65. The elongation-at-break is 70%. To be applied with a trowel or extruded into the suitably-taped sections of the joint (to protect adjacent surfaces). Resistant to contact with hydrocarbons (gasoline and diesel fuel). Horizontal sealing of joints in industrial flooring, even in the presence of chemical attacks and stresses from average-heavy traffic. Vertical sealing of joints in concrete works and products. The application and containment surfaces (joint walls) should be clean, dry, conveniently prepared and adequately resistant: free from dust, grease, soiling, crumbling and/or non-adhering parts and dry. The application surfaces must also be preliminarily treated with Protech Flex Primer. Add component B to component A taking care to pick up all the material contained in the packs, mix thoroughly with a mixer at a low number of revolutions, until a perfectly homogeneous mix is obtained; add the required load amount (component C) continue to mix until a perfectly homogeneous mixture is obtained, indicated by the uniform colour of the mixture. Apply the product mixed by trowelling or with extrusion guns. Do not apply with temperatures below + 5°C or higher than + 35°C and in the presence of surface stagnant water. Approximately 1.25 kg of EG 91 per cubic decimetre of joint volume to be sealed (1250 kg per cubic metre). Packaging: Kit of 5+2.5 kg UM: €/kg

Syntech Pavidamp A three-component formulation, with a fluid epoxy resin base in aqueous emulsion (A + B) to be mixed with the third component (C) consisting of white cement and micro-quartz, specially designed to be used as a primer for cementitious surfaces in the presence of humidity and in conditions of hydraulic counter-thrust. Generally referred to as “wet-bonding”, it is particularly suitable as an anti-humidity barrier for the subsequent laying of parquet. Building connection layers and smoothing cement surfaces; bottom layers for resinous coatings of floorings in the presence of damp subbases; anti-humidity barriers in concrete, brick and stone masonry; surfacings of porosity, cracks and superficial irregularities. As protection from rising damp for bases where operations with polyurea resins SYNTECH POLYUREA will be carried out. The support on which the resin system is to be laid must be suitable for withstanding the stresses resulting from the intended use, such as static or dynamic loads, impacts, thermo-hygrometric dilatations, vibrations, etc. As regards the characteristics of the substrate (maximum humidity, cohesion, strength class, flatness, etc.) and the preparation of the surface that will accommodate the resin system, we recommend the requirements set out in chapter 5 of the UNI 10966 standard ("RESIN SYSTEMS FOR SURFACES HORIZONTAL AND VERTICAL - INSTRUCTIONS FOR DESIGN AND APPLICATION "). In any case, carefully clean and degrease the surfaces, removing any kind of dirt, paint residues or incoherent parts. Evaluate the most convenient type of mechanical preparation (shot peening, sandblasting, hydro-washing, etc.). The surfaces must also be free from discontinuity, and possibly leveled and regularized with products from the FLOOR line or the REPAR line. Apply by roller, brush or spray from 150 to 200 g / m2 of Syntech Primer EP-W to consolidate the substrate and facilitate the adhesion of the subsequent coating. Tiled floors, or floors covered with pre-existing resin, must be subjected to mechanical roughening carried out with shot blasting, milling, bush hammering, etc., until the total elimination of the waterproof crust and the opacification of the surfaces. Remove dust after abrasion. Prepare the mixture of the 2 liquid components (A+B), pouring the contents of the component B in the container of the component A. Mix with drill for about 2 minutes. Add the pre-dosed hydraulic binder (high resistance white cement) to the mixture A+B, and mix with a mixer drill. To disperse the product optimally, pour the powders (component C) a little at a time, continuing to stir with drill, until a homogeneous lump-free mixture is obtained. If it is used as a base: dilute with 10-15% by weight of clean, soft water and apply with a roller or brush. Indicative consumption: 0.4-0.5 kg/m² on regular supports, 0.7-0.9 kg/m² on irregular supports. If it is used for fine finishing coats: load the system A+B+C diluted with 10-15% of fresh clean water, with 60-70% spheroidal quartz (0.04-0.25 mm). Apply with steel trowel or plastering trowel. Indicative consumption: 1-2 kg/m². If it is used for medium finishing coats: load the system A+B+C diluted with 10-15% of fresh clean water, with 70-80% spheroidal quartz (0.1-0.5 mm). Apply with steel trowel or plastering trowel. Indicative consumption: 3-4 kg/m². From 0.50 to 0.60 kg of SYNTYECH PAVIDAMP for each square metre of surface to be covered. Pail 3.8 kg [A] - Pail 1.2 kg [B] - Pail 5 kg [C] - Kit: 1 Pail 3.8 kg [A] + 1 Pail 1.2 kg [B] + 1 Pail 5 kg [C]

2component epoxy paint for the protection of concrete floors, metal structures, etc. Does not contain solvents (100% solids). Features Excellent adhesion. Great penetration power. Good adhesion in wet substrate with high percentage of humidity. Good capacity for reaction at low temperatures and high percentage of humidity. Indoor and outdoor use.